Refractory Cement
Combined with various refractory raw materials and appropriate additives (regulators, water reducing agents) to form various unshaped refractory materials.
CA50
Al2O3: ≥50-53.5%;
Initial Setting Time: ≥45-90min;
Final Setting Time: ≤6min;
72H Compressive Strength: 55-82MPa;
CA70
Al2O3: ≥68.5-71.5%;
Initial Setting Time: ≥120-240min;
Final Setting Time: ≤90-300min;
72H Compressive Strength: 45-65MPa;
CA80
Al2O3: ≥78-81%;
Initial Setting Time: ≥30-150min;
Final Setting Time: ≤90-350min;
72H Compressive Strength: 40-50MPa;
Technical Data
Item/Grade | CA50 | CA70 | CA80 | ||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
A600 | A700 | A900 | CA70 | CA70W | CA70S | CA71 | CA80 | CA80S | |||
Chemical Composition | ω (SiO2) ≤/% | 7.8 | 7.5 | 5.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | |
ω (Al2O3)/% | 50.0 | 51.0 | 53.5 | 68.5-70.5 | 68.5-70.5 | 68.5-70.5 | 69.5-71.5 | 78.0-81.0 | 78.0-81.0 | ||
ω (Fe2O3) ≤/% | 2.5 | 2.5 | 2.5 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | ||
ω (CaO)/% | / | / | / | 28.5-30.5 | 28.5-30.5 | 28.5-30.5 | 27.5-29.5 | 17.5-20.5 | 17.5-20.5 | ||
ω (MgO) ≤/% | / | / | / | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
ω (R2O) ≤/% | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
ω (S) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
ω (Cl) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
Fineness | d50/μm | / | / | / | 11-4 | 8-11 | 6-9 | 10-13 | 5-8 | 5-8 | |
-45μm ≤/% | / | / | / | 8.0 | 5.0 | 5.0 | 8.0 | 5.0 | 5.0 | ||
Setting Time | Initial Setting Time (min) | ≥45 | ≥60 | ≥90 | 120-180 | 30-90 | 180-240 | 150-210 | 30-90 | 90-150 | |
Final Setting Time (min) | ≤6 | ≤6 | ≤6 | 150-240 | 90-180 | 240-330 | 210-300 | 90-180 | 270-360 | ||
Strength (ISO) | Flexural Strength/Mpa | 24h | 6.0 | 6.5 | 8.0 | 7.5-10.0 | 8.0-10.5 | 8.0-10.5 | 8.5-11.0 | 5.0-7.5 | 5.0-7.5 |
72h | 7.0 | 7.5 | 10.0 | 10.0-12.0 | 10.5-12.5 | 10.5-12.5 | 11.0-12.5 | 6.0-8.5 | 6.0-8.5 | ||
Compressive Strength/Mpa | 24h | 45 | 55 | 72 | 40-50 | 45-55 | 45-55 | 50-60 | 30-40 | 30-40 | |
72h | 55 | 65 | 82 | 45-55 | 50-60 | 50-60 | 55-65 | 40-50 | 40-50 | ||
325M ≤/% | 15 | 12 | 8 | / | / | / | / | / | / | ||
Specific Surface Areas ≥/ (㎡/kg) | 300 | 320 | 350 | / | / | / | / | / | / |